ASTM A105

Element

Composition, %

Carbon

0.35 max

Manganese 

0.60–1.05

Phosphorus 

0.035 max

Sulfur 

0.040 max

Silicon 

0.10–0.35

Copper 

0.40 max

Nickel 

0.40 max

Chromium 

0.30 max

Molybdenum 

0.12 max

Vanadium 

0.05 max

Columbium 

0.02 max

Tensile strength, min, psi [MPa] 

70 000 [485]

Yield strength, min, psi [MPa] 

36 000 [250]

Elongation in 2 in. or 50 mm, min, 
%: Basic minimum elongation for walls 5⁄16 in. [7.9mm] and over in thickness, strip tests.

30

When standard round 2-in. or 50-mm gage length or smaller proportionally sized specimen with the gage length equal to 4D is used

22

For strip tests, a deduction for each 1⁄32 -in. [0.8-mm] decrease in wall thickness below 5⁄16 in. [7.9 mm] from the basic minimum elongation of the percentage points

1.5

Reduction of area, min, % 

30

Hardness, HB, max 

187